Structural And Electrochemical Properties Of Fe-doped Nial2o4 Oxides
Résumé: A new spinel solid solution system of Ni1-xFexAl2O4 (0.0 ≤ x ≤ 0.5) was synthesized through sol-gel method. The effect of Fe doping on the nickel aluminate prepared was investigated. The synthesized powders were characterized by means of X-ray diffraction, thermogravimetric and differential thermal analysis, fourier transform infrared spectroscopy, scanning electron microscopy and electrochemical measurements. From the preceding analysis, it can be shown that compounds show a single spinel phase in the temperature range 650-1000°C and the solubility of iron in the NiAl2O4 structure was limited to samples with the iron content x < 0.6. The electrochemical measurements indicate that the catalytic activity is strongly influenced by iron doping. The highest electrode performance is achieved with Ni0.7Fe0.3Al2O4 (i=86.84 mA/cm2) which is ~ 27 times greater than that of NiAl2O4 ( i=3.22 mA/cm2) at E= +0.8V. After one hundred cycles, the stability of the doped electrode with 30% of iron is much better than the undoped electrode
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".