Synthesis And Evaluation Of The Structural, Microstructural, Optical And Magnetic Properties Of Zn1−xcoxo Thin Films Grown Onto Glass Substrate By Ultrasonic Spray Pyrolysis
Résumé: Ultrasound pyrolysis spray technique is used to prepare single-phase thin films of Zn1−xCoxO (x=0–22 at.%). The hexagonal wurtzite structure of the films is confirmed by X-ray diffraction with an average crystallite size estimated in the range of 18–30 nm. The compound structure and stoichiometry of the films are further characterized by energy-dispersive spectroscopy (EDAX). The spectrum analysis agreement great chords between the expected and measured Co atomic content in the films indicating an effective doping. The results also reveal a high solubility of Co into ZnO solid solution at about 14 at.%. For the optical proprieties, the bandgap energy decreases due to the presence of high concentrations of localized states in the thin films. The photoluminescence spectra of all the samples exhibited a broad emission in the visible range. In addition, the magnetic properties of Zn1−xCoxO thin films are found to be strongly influenced by Co doping
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".