Stabilite Magnetique D’un Alliage Nanocristallin A Base De Feco
Résumé: FeCo-based nanostructured powders were produced by mechanical alloying in a planetary ball mill with different milling times. The different physical properties were studied as a function of milling time (h), ranging from 0 h to 96 h, using X-ray diffraction (XRD), and by differential scanning calorimetry (DSC). Some magnetic properties at room temperature were measured by a vibration sample magnetometer (VSM). The saturation magnetisation decreases rapidly during the first 9 h of milling to about 115 emu. A coercivity value Hc of about 71.6 Gauss is obtained after 96 h of milling.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".