دراسة اكسيد الكالسيوم والمنغنيزيوم علي تلبيد مركبي الانثوريد والكوردريت
Résumé: Many studies have been directed at developing alternative ceramics to replace conventional alumina substrate for an increase in semiconductor integrated circuit performance .such as light density, greater pin counts. For these purposes, ceramics substrates should have a low dielectric constant, low thermal expansion coefficient, and sintering temperature less than 1000°c , namely lower than the melting temperature less of copper, silver, or gold. Stoichiometric chemical of Kaolinite and halloysite are Al2O3.2SiO2.nH2O, Kaolin base clay is rarely used for precision electrical and electronic devices because of impurities such as alkaline metal, iron, and titanium oxides that significantly affect electrical insulation and dielectric properties. In this study using kaolin (Djebel debbagh DD1), dense anorthite and cordierite were obtained with low-temperature firing below 1000°c for anorthite and 1400°c for cordierite by controlling the amounts of CaO and MgO respectively, the main constituent was anorthite (kaolin-CaO) and cordiriete (kaolin-MgO) , determined from X-ray diffraction (XRD) analysis.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".