Élaboration Des Couches Minces Otc De Type In2o3:sn Pour Applications Photovoltaïques
Résumé: The present work consists of the deposition and characterization of thin films of indium oxide doped with tin In 2O3 : Sn (ITO) by the electrodeposition method: Effect of annealing temperature. The main objective of our work is to study the effect of annealing temperature on the various properties of In 2O3 : Sn thin films. Three samples were prepared under the same experimental conditions and treated at three different temperatures (200, 300 and 400 °C). Diffraction analysis showed that all the elaborated films present only the In2O3 phase in its cubic structure, therefore these layers are monophasic. The film annealed at 200 °C presents its most intense peak along the (440) direction while the other two films have their most intense peak along the (222) direction. The gap energy of the three layers is almost constant; it varies from 3.89 eV to 3.94 eV. These values are relatively high, which indicates that these films do not absorb in the visible region of the solar spectrum, and the elaborated layers can be used in the manufacture of the window layer of the thin film solar cell. Keywords: In 2O3 :Sn - Electrodeposition - Thin film - Annealing temperature.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".