Nanomechanical Properties Of Nanoconfined Polystyrene Nanoparticles In Nanoblends
Résumé: The role of nanoconfinement on the glass transition temperature (Tg) of polymers has been extensively studied in the thin film geometry. This work looks at the Tg of nanoconfined polystyrene in spherical nanoparticles (27- 200 nm), individually dispersed in crosslinked polybuthylmethacrylate matrices. A reduction of Tg compared to the bulk was observed in PS nanospheres via neutron scattering-mechanical tests and was found to decrease with decreasing diameter for D< 50nm. The general trend of Tg depression in nanospheres was found to be similar to the results on thin film geometry.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".