Analysis Of The Plastic Zone Under Mixed Mode Fracture In Bonded Composite Repair Of Aircraft Structures
Résumé: Material fracture by opening (mode I) is not the only failure criteria responsible for fracture propagation. Many industrial examples show the presence of mode II and mixed mode I + II. In the present work, numerical analyses of the three-dimensional and non-linear finite element method are used to estimate the performance of the bonded composite repair of metallic aircraft structures with a pre-existent damage by analyzing the plastic zone size ahead of repaired cracks under mixed mode loading, to assess the effect of the composite repair system on the plastic zone. The Von Mises stress is used to predict yielding of materials under this loading condition. The extension of the plastic zone, which takes place at the tip of a crack, strictly depends on many variables, such as the yield stress of the material, the loading conditions, the crack size and the thickness of the cracked component. The obtained results have demonstrated that the plastic zone ahead of the crack is significantly reduced by the presence of composite patch materials. Furthermore, parametric analysis has been carried out to evaluate the effect of lay-up and material system variation on the J integral.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".