Heat Treatment And Kinetics Of Precipitation Of Β-mg17al12 Phase In Az91 Alloy
Résumé: This study investigated the effect of aging on the precipitation and kinetics of second phase Mg17Al12 in AZ91 magnesium alloy (Mg-9 wt% Al-1 wt% Zn), using X-ray diffraction, microhardness measurements and differential scanning calorimetric analysis (DSC). With the last instrument, the all samples were heated from room temperature to 400 °C, at heating rates of 10–30 °C/min. The results were supplemented by measuring the average of activation energies, using isothermal treatments by Johnson–Mehl–Avrami (JMA) methods and by non-isothermal treatments using Ozawa, Boswell, Kissinger, Mahadevan, Augis and Bennett methods, were around 67.18 and 62.02 kJ/mol. The frequency factor k0 calculated by the isothermal treatment is equal to 1.24 109 s−1. In non-isothermal treatment, the numerical factor m and the Avrami parameter n is estimated to be approximately equal to 3 and 2.79 respectively. This value corresponding that the bulk nucleation with a constant number of nuclei was dominant in three-dimensional (polyhedron) controlled by interface reaction.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".