A Comparative Structural And Magnetic Study Of Fe100-xpdx(x=15, 20 And 36) Thin Films Deposited On Si (100) And Glass Substrates
Résumé: Various structural and magnetic characterization techniques have been used to investigate Fe100-xPdx (x=15, 20 and 36) thin films deposited onto silicon and glass substrates, by thermal evaporation technique. X-ray diffraction analysis shows the presence of supersaturated solid solution with bcc structure for Pd concentrations of 15% and 20%. However, for 36% of Pd, in addition to the supersaturated α-FePd (bcc) phase, another disordered FePd3 phase with fcc structure is present. At 20 at% Pd, the magnetic characterization shows a saturation of the bcc (α-FePd) phase and the appearance of the fcc phase. The correlation between the structure and magnetic properties allows us to compare the two substrates effects on deposited thin films. As results, the measurements indicate that the grain size D, the thin film thickness and the d(110) spacing significantly affect the magnetic coercivity HC. The Fe-Pd alloys deposited on a monocrystalline Si (100) and glass substrate show that the coercivity HC is given by the random anisotropy model. & 2015
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".