High Temperature Annealing Of Sprayed Sno2 : F Layers In A Silicon Solar Cell Process With Screen-printed Contacts
Résumé: In order to improve the solar cell conversion efficiency, a thin film of doped tin oxide (SnO2: F) has been deposited by the spray-pyrolysis technique on a monocrystalline diffused silicon wafer. Subsequently, the layer must undergo the firing step of screen-printed contacts with temperatures up to 830 °C. After annealing, one notices with the naked eye the appearance of speckles disturbing the uniformity of the as-deposited blue-coloured SnO2:F. Characterizations such as XPS, FTIR, RBS, XRD, SEM, Hall Effect, four point probe...etc, are all consistent to reveal a net increase of the SnO2:F layer resistivity which leads to efficiency degradation. Annealing the thin films under CO and 90% N2–10% H2 atmospheres was investigated to seek possibilities to preserve the expected improvements. Unlike forming gas, CO reducing ambient was found to be very effective for the high temperature contact firing with no thin film conductivity deterioration
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!