Mechanism Of Action Of Tin On The Semi-conductive Properties Of Pbo Layer In Lead Acid Battery

Résumé: Although antimony in alloys for lead-acid batteries has better mechanical and electrochemical performance, it reduces the excessive potential for hydrogen evolution, resulting in excessive water loss and self-discharge of the battery. This paper aims to examine the action of tin in PbSn using different techniques. In this work, the addition of tin in PbCa was intended to suppress the premature capacity loss (PCL) caused by the substitution of antimony in the PbSb alloy by calcium that has good mechanical properties and a high hydrogen evolution potential (200 mV higher than that of antimony). This substitution induces the formation of a passive film composed mainly of α-PbO. The mechanism of action of tin on the anodic film obtained at 700 mV vs. Hg/Hg2SO4/K2SO4 saturated electrode with Pb – (0–5) wt.% Sn in 0.5 mol/L sulfuric acid solution at 25 °C was studied using electrochemical impedance spectroscopy (EIS), AC voltammetry, Mott–Schottky plots and X-ray diffraction (XRD) of the film obtained. It was found that tin stops the growth of the anodic film due to the co-precipitation of certain conductive oxides which reduce the thickness of the passive film and increase its conductivity. A mechanism of action of tin on the electrochemical behavior of the anodic film was suggested based on the results.

Publié dans la revue: