Residual Stress, Mechanical And Microstructure Properties Of Multilayer Mo 2 N/crn Coating Produced By R.f Magnetron Discharge
Résumé: We have investigated the effect of the period thickness of the multilayer Mo 2 N/CrN deposited on Si substrate produced by reactive magnetron sputtering. Mo 2 N presents a face centered cubic structure and CrN an orthorhombic one. The residual stress of the coatings was determined by the measurement of the substrate curvature. The microstructure of the multilayer was investigated from the X-ray diffraction and scanning electron microscopy (cross section images). The residual stresses resulting from the deposition of the different bi-layer thickness were measured and correlated to the structural properties of the coating as well as the nanoindentation analysis of the coating. The stresses are compressive and tensile for the individual Mo 2 N and CrN layer respectively. The result shows that an increase of the multilayer coatings Mo 2 N/CrN thicknesses induce an increase of the hardness and the elastic modulus, in the other hand the tensile stress increases. The shift of the XRD diffraction peak (1 1 1) of Mo 2 N at high angle which means the reduction of the residual stress is in good agreement with the residual stresses measurements
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".