Effects Of Current Density On Ni–p Coating Obtained By Electrodeposition
Résumé: In this work, Ni–P coatings are deposited on the steel substrate by electro-deposition from a solution containing nickel sulfate and sodium hypophos-phite (NaH2PO2). The effect of the current density on the morphology, phase structure, microhardness, and corrosion performance of the Ni–P coatings are studied. Scanning electron microscopy and energy dispersive X-ray anal-ysis and X-ray diffraction are used to study the morphological, composition and phase structure. The corrosion performance of the coatings is evaluated by weight loss, electrochemical impedance spectroscopy and Tafel polariza-tion. Results showed that the morphology of the electrodeposited Ni–P alloys coatings has spherical grains for all the samples, and the Ni3P phases are formed all over the microstructure of the coatings. It is observed that the phosphorus content and microhardness are dependent on the current density. The corrosion tests show that 5 A⋅dm−2 current density is the optimal value which gives the best protective coating against corrosion. It also exhibits su-perior microhardness originated from the higher Ni3P amount.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".