Γ-radiation, Chemical Synthesis Of Ce3+ : Gd2si2o7/sio2 Nanocomposite
Résumé: In this work, Ce3+:Gd2Si2O7/SiO2(0.1 mol% Ce3+) nanocomposite powders were successfully synthesized via γ-irradiation, followed by thermal treatment at 900 °C for 2h.The radiations were carried out in a 60Co γ-source chamber at a dose up to 50 kGy. The structural, morphological and optical properties were investigated using X-ray diffraction analysis (XRD), Raman spectroscopy, Transmission electron microscopy (TEM) and Photoluminescence (PL) spectroscopy. XRD analysis reveals the formation of pure orthorhombic δ-Gd2Si2O7 Gadolinium pyrosilicate (δ-GPS)crystalline phase. The average particles size ranges from 30 to 50 nm when the γ-doses increase up to 50 kGy. Raman scattering shows that the intensity of Raman bands significantly increases with increasing of γ-doses. TEM observations show well dispersed spherical GPS nanoparticles within the silica glass host and confirmed the particles size and size distribution dependence on the γ-irradiation dose. Finally, photoluminescence measurements show that the emission intensity corresponding to 5d-4f transition of Ce3+increases with increasing of γ-irradiation dose due to high purity, better crystallinity and uniform distribution of Ce3+ions into GPS nanostructures
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".