Thermal, Electrochemical And Mechanical Properties Of Shape Memory Alloy Developed By A Conventional Processing Route
Résumé: A Cu based shape memory alloy (Cu-Al-Ni) having a composition 83% Cu, 14% Al, 3% Ni, was developed and studied to determine the shape memory effect. Powder of Cu, Al and Ni was melted in a pit furnace at about 15500C, and casted alloy was heat treated at 8500C for a period of 50 minutes followed by water quenching. Microstructure characterization of alloy (Cu-Al-Ni) was carried out to determine the pre-quenched (cast structure) and quenched martensitic structure. The microstructure analysis of developed samples showed needle like structure of quenched martensite after heat treatment. It has a very good resemblance with structure of casted shape memory alloy obtained from the vacuum induction process. The Vickers hardness test was also performed. Quenched microstructure with improved hardness than pre-quenched structure was observed.
Mots-clès:
Publié dans la revue: Revue des Sciences Fondamentales Appliquées
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".