Synthese Et Proprietes Physiques D'oxyde Mixtes A Base De Lanthane Calcium Et Aluminium.
Résumé: La1âxCax Al O3 (0 ⤠x ⤠0.6) perovskite-type oxides were prepared by co- precipitation method using metal nitrate salts as cation precursors and NaOH solution as the precipitating agent. Differential thermal analysis (DTA) and thermogravimetric analysis (TGA) results indicate that decomposition of the precursor to the oxide begins at \~ 800°C. Powder X-ray diffraction (XRD) patterns confirm the formation of the perovskite phase. Show two IR analysis active vibrational modes at 450 and 670 cmâ1 which are assigned to AlO6 octahedra of the oxide matrix. The microstructure and morphology of the compounds show that the particles are nearly spherical in shape and are agglomerated. The electrochemical study by cyclic voltammetry and chronoamerometry shows that the richest sample in calcium has the best catalytic activity for the evolution of oxygen and the oxidation of methanol
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".