Reliability Analysis Of Bwr Piping Including The Effect Of Residual Stresses
Résumé: Welding residual stress is one of the most important factors of stress corrosion cracking (SCC) growth in pressure boundary piping. A probabilistic fracture mechanics model of structural reliability is described that considers failure to occur as the result of subcritical and catastrophic growth of pre-existing cracks that escape detection. The model considers cracks to be two-dimensional and is capable of treating many of the input parameters as random variables and can consider arbitrary inspection schedules. Residual stresses play a very important role in the initiation and growth of stress corrosion cracks. Hence they are important in the analysis of reliability of sensitized welds in BWR piping; our model includes extensive provisions for their consideration.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".