Impact Of In-service Inspection On The Reliability Of Small Piping
Résumé: Abstract. This paper describes the cracking of stainless steel piping under Inter-granular Stress Corrosion Cracking (IGSCC) conditions using probabilistic fracture mechanics that predict the impact of in-service inspection (ISI) programs on the reliability of specific nuclear piping systems that have failed in service. The IGSCC is characterized by a single damage parameter, which depends on residual stresses, environmental conditions, and the degree of sensitization. The Probability of Detection (POD) curves and the benefits of in-service inspection in order to reduce the probability of the leak for nuclear piping systems subjected to IGSCC were discussed. The results show that an effective ISI requires a suitable combination of crack detection and inspection schedule. An augmented inspection schedule is recurred for piping with fast-growing crack to ensure that the inspection is done before the cracks reach critical sizes and that the use of a better inspection procedure can be more effective than a tenfold increase in the number of inspections of inferior quality.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".