Effects Of Remedial Actions On Small Piping Reliability
Résumé: This article describes probabilistic calculations that address intergranular stress corrosion cracking of stainless steel piping; a degradation mechanism of major concern to nuclear pressure boundary integrity. The objective is to simulate the cracking of stainless steel piping under intergranular stress corrosion cracking conditions, and to evaluate the structural reliability using remedial actions for intergranular stress corrosion cracking that are limited to benefits of in-service inspections and the induction heating stress improvement process. The results show that an effective in-service inspection requires a suitable combination of flaw detection capability and inspection schedule, and it has been suggested that the residual stresses could be altered to become favorable, thereby improving the reliability piping.
Mots-clès:
Nos services universitaires et académiques
Thèses-Algérie vous propose ses divers services d’édition: mise en page, révision, correction, traduction, analyse du plagiat, ainsi que la réalisation des supports graphiques et de présentation (Slideshows).
Obtenez dès à présent et en toute facilité votre devis gratuit et une estimation de la durée de réalisation et bénéficiez d'une qualité de travail irréprochable et d'un temps de livraison imbattable!
Aucun fichier associé
Si le fichier est volumineux, l'affichage peut échouer. Vous pouvez obtenir le fichier directement en cliquant sur le bouton "Télécharger".